Glazing for glass in corner cupboard doors
- Thread starter carheir
- Start date
You are reading the forum of the Society of American Period Furniture Makers — people who build and study American period furniture.
Membership brings the whole forum, the annual journal and quarterly magazine, the members’ gallery and workbench, and chapters across the country. About membership
R
rococojo
Guest
Hi Mike, I think the first method used to fix glass, would be the simplest way?
And that would be with timber beads, just fixed by nailing in place, this method would only be altered to stop, Draft, Shock & Rain. (Outside work).
Design would take over then.
The straight glazed in look you are restoring, would be down to the furniture designer.
No need for stopping, shock, wind or water, as it is inside a building.
Joseph Hemingway
And that would be with timber beads, just fixed by nailing in place, this method would only be altered to stop, Draft, Shock & Rain. (Outside work).
Design would take over then.
The straight glazed in look you are restoring, would be down to the furniture designer.
No need for stopping, shock, wind or water, as it is inside a building.
Joseph Hemingway
I pulled this from the NAWCC site where this topic as discussed. I think it is much easier to use a glazing compound on a curved door than it is to put in sticks. to be accurate glazing is the glass,and the operation of installing the glass, glazing compound is the stuff you asked about. Here is the quoted text:
"Hi,
Someone mentioned whiting (calcium carbonate), which is commonly available from any/all hardware and paint stores for thickening paint or for sports fields.
I mix up whiting with pigment powder to get the color I want and then mix with shellac to a stiff consistency. It is easily reversible, can be colored as desired. If you are already working with shellac, you should have all the ingredients, except the whiting.
Personally, I don't like the oil-based putties but I'd use them before I ever used Rock Hard on an antique.
Craig
and also:
I think that shellac based putty is what the clock makers used originally.A sample of the old putty will dissolve in alcohol leaving the whitting and pigment.The clock makers did not have months to wait for linseed based putty to dry,and it would have softened up in the peddler's wagon in the summer heat,while shellac based putty dries in a day or two.
David
I haven't tried this but it makes sense, see if the glazing compound on your restoration dissolves in alcohol and let use know how this works.
Mike
"Hi,
Someone mentioned whiting (calcium carbonate), which is commonly available from any/all hardware and paint stores for thickening paint or for sports fields.
I mix up whiting with pigment powder to get the color I want and then mix with shellac to a stiff consistency. It is easily reversible, can be colored as desired. If you are already working with shellac, you should have all the ingredients, except the whiting.
Personally, I don't like the oil-based putties but I'd use them before I ever used Rock Hard on an antique.
Craig
and also:
I think that shellac based putty is what the clock makers used originally.A sample of the old putty will dissolve in alcohol leaving the whitting and pigment.The clock makers did not have months to wait for linseed based putty to dry,and it would have softened up in the peddler's wagon in the summer heat,while shellac based putty dries in a day or two.
David
I haven't tried this but it makes sense, see if the glazing compound on your restoration dissolves in alcohol and let use know how this works.
Mike
R
rococojo
Guest
carheir said:I am restoring a corner cupboard that was in a fire and noticed that the glass (what is left) was glazed in. Any thoughts as to what was used back then to glaze glass in place? Any help would be appreciated.
Mike Shelley
Carolina Heirlooms
mshelley@nc.rr.com
Mike, did I miss read your Q? (I think not, after re-reading it) I was explaining the first method used, only to illustrate why your job was glazed in, without any putty.
(Glazing compound) these were developed to correct the earlier mistakes, which I talked about in my reply, now if you ask when putty was first made/used?
That is a different question. Sorry if I confused anyone.
Joseph Hemingway
R
rococojo
Guest
Mike, No I have no alternative, as this was stated in the following post by mike, and you are to try as an alternative soon, its more a Contradiction, than confusion? Sourly,carheir said:Joseph,
I can see where the confusion lies. What I meant to ask was "What kind of glazing compound" was used back in the day. Unless you have a better alternative, I will try the whiting,pigment, shellac formula and see if that will work.
Thanks,
Mike
if if, forget it?
no beans Spilled, hoping the compound is ok for you.
Joseph Hemingway
If this discussion was useful, there are twenty years of them here. Join SAPFM to take part — the forum, the journal, the magazine and the members’ gallery come with membership.